Austenitic stainless steels are widely used in ZFV company valve production. Normal austenitic stainless steel indclude A351 CF8M, A351 CF8, A351 CF3M, A351 CF3, A351 CF8C, A351 CN7M, A 182 F316, A 182 F304,A 182 F316L, A 182 F304L, A 182 F347, A 182 F321 etc. These row material need to be carried out proper heat treatment to achieve certain mechanic properties which meet requirement of international standard such as ASTM standard. Generally the heat treatment type to austenitic stainless steel include solution treat and quenching.

Solution treatment is to heat the metal material to specific high temperature which be mentioned on material stardard, hold the temperature for certain time. here take the A182 F316 as sample, heat metal to temperature 1080 degree C, hold this temperature for 3-4 hours, next quench the metal .

Quenching is the process to cool a metal at a more rapid rate, comparing with annealing and normalizing. In ferrous alloys, this process will produce a harder metal, while non-ferrous alloys will usually become softer than normal. Cooling can be done by liquid such as water, oil, a polymer dissolved in water, or a brine. Austenic stainless steel quenched to become fully corrosion resistant, and wearing resistant. Ally row material of ZFV valve be carried out heat treatment .

Zhejiang Zhengfeng valve

Related Products